Home / Product Information / Product Domain / Thermoplastic Elastomers (TPEs) / JSR EXCELINK®

Product Information

Thermoplastic Elastomers (TPEs)

JSR EXCELINK®(PDF 104KB)

JSR EXCELINK1200~1800

▌Characteristics
  • - Dynamic vulcanized TPO
  • - High melt flow and good injection moldability
  • - Excellent adhesion with cured rubbers
  • - Wide Range of hardness(20-80(DuroA))

▌Typical Applications
Properties 1200B 1300B 1301B 1303B 1404B 1504B 1600B 1601B 1700B 1703B 1800B 1805B 1810B
Hardness
(15sec)
25 35 37 38 45 54 65 64 72 73 80 80 80
Density
(g/cm3)
0.88 0.88 0.88 0.88 0.88 0.89 0.88 0.88 0.88 0.89 0.89 0.89 0.9
MFR
230℃×21N
(g/10min)
1 1.4 1 1 2 2 4.9 10 11 2 33 16 60
at 100%
elongation
(MPa)
0.7 0.8 0.9 0.9 0.9 1.5 2.1 2 2.5 2.6 3 3.2 3.1
Tensile
strength
(MPa)
2.6 3.6 3.3 3.3 3.4 4.4 6.3 6.2 7.3 7.3 9.5 7.5 6.6
Elongation
at break
(%)
470 760 660 650 620 650 610 820 590 730 650 740 610
CS
70℃×22hrs
(%)
28 39 34 40 34 44 50 44 56 57 59 58 56

JSR EXCELINK3400~3700

▌Characteristics
  • - Original crystalline pseudo-crosslinkage structure
  • - Excellent rubber elasticity (compression set) equivalent to that of crosslinked rubbers
  • - Uniform closed cell and high expansion ratio obtained as TPO foams
  • - Crosslinking agent free, clean elastomer

▌Typical Applications
  • - Packing, Seals, etc.

Properties Unit Testing
Method
3400B 3600B 3700B
Hardness
(15sec)
Duro A ISO 868 33 58 65
Density g/cm3 ISO 1183 0.88 0.88 0.88
MFR 230℃×49N g/10min ISO 1133 3 0.9 1
230℃×98N 14 5 5
at 100% elongation MPa ISO 37(I) 0.7 1.6 2
Tensile strength MPa JIS K6251 4.5 10.6 8.3
Elongation at break %   >1000 1030 910
Tear Strength TR-B kN/m ISO 34 B (a) 22 34 42
CS
70℃×22hrs
% ISO 815
JIS K6262
41 37 41
Gloss % ISO 2813 17 28 41
Shrinking percentage % JSR Method 0.6 0.7 0.7

JSR EXCELINK4700

▌Characteristics
  • - High melt flow and good injection moldability
  • - Excellent oil resistance
  • - Excellent low-tempereture properties

▌Typical Applications
  • - Oil resistant tube, hose, packing, etc.
  • - replacement of NBR rubbers

Properties Unit Testing Method 4700 Competior TPO
Density g/cm3 JIS K7112 1 1
Hardness
(15sec)
  JIS K6253 86 72
MFR g/10min JIS K7210
230℃×98N
112 4
at 100% elongation MPa JIS K6251 5.7 2.3
Tensile strength MPa 9 4
Elongation at break % 240 230
CS % JIS K6262
22hrs,70℃
41 40
Oil resistance
(IRM903)
120℃×70hrs
Sc(TB) % -29 -18
Sc(EB) % -45 -17
CH -1 -6
△V % -4 -5
Oil resistance
(Fuel-C)
23℃×70hrs
Sc(TB) % -36 -40
Sc(EB) % -36 -30
CH   -9 -12
△V % 20 33
Aging Test 120℃×200hrs
Sc(TB) % 4 8
Sc(EB) % -6 -9
CH   3 -1
Brittle Temperature   -36 -35

Contact Us
Petrochemical Products Div.
Specialty Elastomer Dept. Alloy Team
Headquarters
1-9-2, Higashi-Shimbashi, Minato-ku, Tokyo 105-8640, Japan
TEL: 81-3-6218-3624 FAX: 81-3-6218-3697
<Products>
  • EXCELINK
Petrochemical Products Div.
Specialty Elastomer Dept. TPE Team
Headquarters
1-9-2, Higashi-Shimbashi, Minato-ku, Tokyo 105-8640, Japan
TEL: 81-3-6218-3625 FAX: 81-3-6218-3697
<Products>
  • RB/TR/SIS/DYNARON